| Place of Origin: | China |
|---|---|
| Brand Name: | Laurel |
| Model Number: | HSB-08 |
| Minimum Order Quantity: | Customer request |
| Packaging Details: | wooden pallets and wooden cases |
| Delivery Time: | 30days |
| Supply Ability: | 1000ton per month |
| Application: | Steel And Metallurgy Industry | Material: | Plastic |
|---|---|---|---|
| Customization: | Based On Request Or Supply Suggestion | Feature: | High Temperature Resistant |
| Size: | Standard | Usage: | Furnaces And Kilns |
| Color: | Assorted | Educational Value: | STEM |
| Certifications: | ASTM, CPSIA | Quantity: | 100 Pieces |
| Country Of Origin: | China | Compatibility: | Interlocking |
| Durability: | High | Weight: | Lightweight |
| Shape: | Rectangular | ||
| Highlight: | refractory bricks,refractory fire bricks |
||
Ingot Casting Of Steel Used Fire Clay Aluminum Bricks Composition
We can offer a complete range of Ingot Casting Of Steel Used Fire Clay Aluminum Bricks Composition. In order to meet the specific requirements of each steel plant, we has set up a vast assortment of moulds and is therefore in a position to produce custom-made products or special shapes according to different production requirements.
Center brick, have a certain strength, have better heat insulation, sound insulation performance, winter indoor wall does not appear the phenomenon of condensation, and the price is low. Although various new wall materials are constantly appearing, the sintering brick will be used as a main material for masonry construction for some time to come. It can be used for building maintenance structure, masonry column, arch, chimney, kiln body, channel and foundation etc. It can be used with lightweight aggregate concrete, aerated concrete, rock wool and other heat insulation materials. In the masonry, suitable reinforcement or steel mesh can be used as reinforcement masonry, instead of reinforced concrete column and underbeam.
Technical data
| Description | 40% | 50% | 60% | 70% | 80% | |
| Bulk Density | g/cm3 | 2.15 | 2.2 | 2.3 | 2.4 | 2.5 |
| Apparent Porosity | % | 24 | 24 | 24 | 23 | 23 |
| Cold Crushing Strength | MPa | 30 | 40 | 45 | 50 | 55 |
| Refractoriness | ℃ | 1710 | 1730 | 1750 | 1800 | 1830 |
| Softening temperature under load | ℃ | 1350 | 1430 | 1450 | 1500 | 1550 |
| Chemical Composition | % | |||||
| -Al2O3 | 40 | 50 | 60 | 70 | 80 | |
| -Fe2O3 | 2.5 | 2 | 2 | 2 | 2 |