| Place of Origin: | Zibo, China |
|---|---|
| Brand Name: | Laurel |
| Certification: | ISO9001 |
| Model Number: | Laurel-03 |
| Minimum Order Quantity: | 20ton |
| Packaging Details: | packed on wooden pallets, with water-proof cover, and tightened with plastic/steel bandages |
| Delivery Time: | 20~30 days |
| Payment Terms: | T/T;L/C |
| Supply Ability: | 10000 ton/Year |
| Classification: | HA60; HA70; HA75; HA80 | Product Name: | Insulation Refractory |
|---|---|---|---|
| Shape:: | Brick | Feature:: | High Temperature Resistant,bulk Density |
| Usage: | Linings, Furnaces And Kilns Etc | Material:: | Alumina Brick |
| High Light: | high alumina brick,high temperature refractory |
||
High Alumina Refractory Fire Bricks For Ceramic Tunnel Kiln , Iron Making Furnaces Firebrick
Description:
Laurel high alumina bricks are produced with selected bauxite chamotte by advanced process and strict quality control. The main mineral components are corundum and mullite phases. It features excellent high temperature mechanics and chemical corrosion resistance.
The most competitive price,good quality,safty packing,prompt delivery time,and excellent after-sales services.
Lower ferric Oxide,lower porosity,higher refractoriness,higher density,higher CCS and exact tolerance.
Features
1.Resisting high temperature
2.Great bulk density
3.Low iron content
4.Good eroding resistance
Applications:
1. Steel furnaces
2. Iron making furnaces
3. Glass kiln
4. Ceramic tunnel kiln
5. Cement kiln
Specifications:
Ordinary High alumina brick
|
Item |
HA60 |
HA70 |
HA75 |
HA80 |
|
AL2O3(%) |
≥60 |
≥70 |
≥75 |
≥75-80 |
|
SIO2(%) |
32 |
22 |
20 |
≥18 |
|
Fe2O3(%) |
≤1.8 |
≤1.8 |
≤1.8 |
≤1.8 |
|
Refractoriness °C |
1790 |
＞1800 |
＞1825 |
≥1850 |
|
Bulk density,g/cm3 |
2.4 |
2.45-2.5 |
2.5 |
2.55-2.6 |
|
Softening temperature under load |
≥1470 |
≥1520 |
≥1530 |
≥1550 |
|
Apparent porosity,% |
22 |
＜21 |
＜21 |
＜20 |
|
Cold Crushing strength Mpa |
≥45 |
≥50 |
≥54 |
≥60 |
Phosphate bonded high alumina bricks
|
Item |
LAP75 |
LAP77 |
LAP85 |
|
AL2O3 % |
≥75 |
≥77 |
≥80-85 |
|
Fe2O3 % |
≤3.0 |
≤3.0 |
≤1.8 |
|
Ca0 % |
≤0.6 |
≤0.6 |
≤0.6 |
|
Refractoriness °C |
≥1800 |
≥1800 |
≥1850 |
|
Bulk density g/cm3 |
≥2.65 |
≥2.70 |
≥2.80 |
|
Cold crushing strength MPa |
≥60 |
≥64 |
≥110 |
|
Refractoriness under load 0.2MPa °C |
≥1350 |
≥1300 |
≥1350 |
|
Application |
Used for high temperature parts lining of cement rotary kiln |
Used for Badly worn parts of cement rotary kiln |
|