| Product Name: | Insulation Refractory | Shape:: | Brick |
|---|---|---|---|
| Feature:: | Acid Erosion Resistance.,light Weight | Usage: | Glass Furnace ,Blast Furnace , Coke Oven |
| Material:: | Silica Brick; | Work Temperature: | 1650º C |
| High Light: | high alumina brick,high temperature refractory |
||
High Temp Refractory Fire Brick , Silica Bricks For Glass Blast Furnace , Coke Oven
Description:
Laurel can produces a large range of silica brick for many kind of industry usage.
SiO2 content: Above 95%.
Al2O3 content: Below 1.0%.
Usage: Hot-blast stove.
Our factory product various kinds of refractory products. The products can be made according with the customers' requirement.
Features:
Applications:
Specifications:
Technical data
|
Silica brick for glass furnace |
|||||||
|
Item: |
GF-96A |
GF-96B |
GF-95A |
GF-95B |
|||
|
SiO 2 |
≥96 |
≥96 |
≥95 |
≥95 |
|||
|
Fe 2 O 3 |
≤0.8 |
≤1.0 |
≤1.2 |
≤1.2 |
|||
|
Apparent porosity % |
≤22(24) |
||||||
|
Cold Crushing Strength MPa |
Brick below20KG |
≥35(30) |
|||||
|
Brick ≥20KG |
≥30(25) |
||||||
|
Refractoriness under load ºC |
≥1680 |
≥1670 |
≥1660 |
≥1650 |
|||
|
True density g/cm ³ |
≤2.34 |
≤2.34 |
≤2.35 |
≤2.35 |
|||
|
Silica brick for coke oven |
|||||||
|
Item: |
CO-94A |
CO-94B |
|||||
|
SiO2: % |
≥94 |
≥94 |
|||||
|
Al 2 O 3 : % |
≤ 1.5 |
≤ 1.5 |
|||||
|
Fe2O3: % |
≤ 1.5 |
≤ 1.5 |
|||||
|
Refractoriness under load 0.2Mpa |
≥ 1650ºC |
≥ 1650ºC |
|||||
|
Apparent porosity: % |
≤ 22 |
≤ 24 |
|||||
|
Bulk density: g/cm ³ |
≤ 2.34 |
≤ 2.35 |
|||||
|
Cold crushing strength: MPa |
≥30 |
≥25 |
|||||
|
Permanent linear change % (1450ºC ×2h) |
0~0.2 |
0~0.2 |
|||||
|
Thermal expansion(1000ºC) |
≤1.28 |
≤1.30 |
|||||
|
Silica brick for hot blast furnace |
|||||||
|
Item |
HBF-95 |
||||||
|
SiO2 |
≥ 95 |
||||||
|
Al2O3 |
≤ 1.0 |
||||||
|
Fe2O3 |
≤1.3 |
||||||
|
Apparent porosity % |
≤22(24) |
||||||
|
Cold crushing strength MPa |
≥45(35) |
||||||
|
Remaining quarts % |
≤1.0 |
||||||
|
Refractoriness under load ºC |
≥1650 |
||||||
|
Creep(0.2Mpa ×1550ºC×50h) % |
≤0.8 |
||||||
|
Thermal expansion coefficient (1000ºC) % |
≤1.25 |
||||||
|
Apparent density g/cm ³ |
≤2.32 |
||||||