| Classification: | High Duty, Super Duty | Product Name: | Refractory Fireclay |
|---|---|---|---|
| Shape:: | Brick | Feature:: | High Temperature |
| Usage: | Metal Mixer Furnace , Blast Furnaces | Temperature Range: | Above 1650º C |
| High Light: | refractory fire bricks,clay fire bricks |
||
High Temperature Fire Clay Bricks, Fireclay Bricks For Metal Mixer Furnace, Blast Furnaces
Dense and Low Porosity Fire Clay Brick
The most competitive price,good quality,safty packing,prompt delivery time,and excellent after-sales services.
Lower ferric Oxide,lower porosity,higher refractoriness,higher density,higher CCS and exact tolerance.
Description:
The low Porosity clay refractory bricks are made of super calcined flint clay and calcined bauxite, With high Pressure formed and high temperature sintered. Due to its low apparent porosity, Strong resistance to erosion and high refractoriness under load, They are wildly used in Glass kiln, Blast furnace, Metal mixer Furnace, Hot metal mixer ladle, Coke dry quenching devices , etc.
Features:
1. Low porosity,High bulk density.
2. Good Cold Crushing strength.
3. High refractoriness under load.
4. High mechanical strength.
5. Good resistance to erosion.
Applications:
1. Glass kiln
2. Blast furnace
3. Metal mixer Furnace,
4. Hot metal mixer ladle
5. Blast furnaces
Specifications:
Technical data
|
Item |
High duty |
Super duty |
|
AL2O3% |
38-42 |
42-45 |
|
Fe2O3% |
1.8 |
1.7 |
|
SiO2% |
56% |
53% |
|
Refractoriness |
1730 |
1750 |
|
Apparent Porosity% |
17Max |
17Max |
|
Refractoriness under load at 0.2MPa |
1420 |
1450 |
|
cold crushing strength ≥ |
40Min |
45Min |
|
Linear Change on reheating 1450C*3H |
-2+0 |
-0.1+0.05 |
|
BD g/cm3≥ |
2.2-2.4 |
2.3-2.4 |