| Place of Origin: | Zibo, China |
|---|---|
| Brand Name: | Laurel |
| Certification: | ISO9001 |
| Model Number: | Laurel-03 |
| Minimum Order Quantity: | 20ton |
| Price: | FOB:225~530/TON |
| Packaging Details: | packed on wooden pallets, with water-proof cover, and tightened with plastic/steel bandages |
| Delivery Time: | 20~30 days |
| Payment Terms: | T/T;L/C |
| Supply Ability: | 10000 ton/Year |
| Thermal Shock Resistance: | Good | Refractoriness: | ≥1580℃ |
|---|---|---|---|
| Packing: | Wooden Pallet Or As Per Customer's Request | Chamotte Brick Advantage: | High Refractoriness |
| Material: | Fire Clay | Application: | High Temperature Industrial Furnaces |
| Bulk Density: | ≥2.1g/cm3 | Port: | Tianjin |
| Type: | Recycling Granulate Extrusion Line | Feature: | DDD Low Porosity, Low Iron, Low Creep |
| Shape: | Rectangular | Usage: | Hot Metal Mixer Ladle |
| Raw Material: | Alumina | Sample: | Freely Provided |
| Processing Service: | Punching, Moulding | ||
| Highlight: | clay fire bricks,fired clay brick |
||
Environmental high alumina refractory brick higher refractoriness
Description:
Laurel high alumina bricks are produced with selected bauxite chamotte by advanced process and strict quality control. The main mineral components are corundum and mullite phases. It features excellent high temperature mechanics and chemical corrosion resistance.
Features
1.Resisting high temperature
2.Great bulk density
3.Low iron content
4.Good eroding resistance
Specifications:
Ordinary High alumina brick
|
Item |
HA60 |
HA70 |
HA75 |
HA80 |
|
AL2O3(%) |
≥60 |
≥70 |
≥75 |
≥75-80 |
|
SIO2(%) |
32 |
22 |
20 |
≥18 |
|
Fe2O3(%) |
≤1.8 |
≤1.8 |
≤1.8 |
≤1.8 |
|
Refractoriness °C |
1790 |
＞1800 |
＞1825 |
≥1850 |
|
Bulk density,g/cm3 |
2.4 |
2.45-2.5 |
2.5 |
2.55-2.6 |
|
Softening temperature under load |
≥1470 |
≥1520 |
≥1530 |
≥1550 |
|
Apparent porosity,% |
22 |
＜21 |
＜21 |
＜20 |
|
Cold Crushing strength Mpa |
≥45 |
≥50 |
≥54 |
≥60 |
Phosphate bonded high alumina bricks
|
Item |
LAP75 |
LAP77 |
LAP85 |
|
AL2O3 % |
≥75 |
≥77 |
≥80-85 |
|
Fe2O3 % |
≤3.0 |
≤3.0 |
≤1.8 |
|
Ca0 % |
≤0.6 |
≤0.6 |
≤0.6 |
|
Refractoriness °C |
≥1800 |
≥1800 |
≥1850 |
|
Bulk density g/cm3 |
≥2.65 |
≥2.70 |
≥2.80 |
|
Cold crushing strength MPa |
≥60 |
≥64 |
≥110 |
|
Refractoriness under load 0.2MPa °C |
≥1350 |
≥1300 |
≥1350 |
|
Application |
Used for high temperature parts lining of cement rotary kiln |
Used for Badly worn parts of cement rotary kiln |
|
Competitive Advantage: